产品说明
项 目 | 实验方法 | 60N | 100N | 150N | 150N | 250N | 350N | 400N | 500N | 750N | 900N | 120BS | |
颜色/赛氏号 | GB/T3555 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+30 | ﹥+24 | +13 | +24 | |
运动粘度(40℃)/mm2/s | GB/T265 | 10.63 | 22.44 | 29.17 | 31.92 | 55.37 | 65.1 | 81.91 | 96.07 | 157.9 | 187.0 | 249.9 | |
运动粘度(100℃)/mm2/s | GB/T265 | 2.567 | 4.089 | 5.104 | 5.074 | 7.371 | 8.358 | 9.64 | 10.85 | 15.7 | 17.40 | 21.29 | |
粘度指数 | GB/T1995 | 53 | 65 | 102 | 78 | 90 | 97 | 94 | 96 | 102 | 100 | 101 | |
闪点(开口)大于, ℃ | GB/T3536 | 164 | 190 | 208 | 202 | 230 | 242 | 246 | 256 | 272 | 279 | 286 | |
倾点/℃ | GB/T3535 | ﹤-40 | ﹤-40 | -36 | ﹤-40 | -35 | -28 | -25 | -20 | -18 | -19 | -15 | |
浊点/℃ | GB/T6986 | ﹤-24 | -13 | -30 | -21 | -24 | -10 | -15 | -10 | +1 | +10 | +14 | |
密度(20℃)Kg/m3 | GB/T1884 | 0.8652 | 0.8653 | 0.8543 | 0.8663 | 0.8665 | 0.8642 | 0.8704 | 0.8676 | 0.8681 | 0.8693 | 0.8707 | |
硫含量/ppm | GB/T0689 | 0.3 | 0.33 | 0.47 | 0.32 | 0.35 | 0.51 | 0.93 | 0.25 | 0.35 | 0.35 | 0.37 | |
氮含量/ppm | SH/T0657 | 0.21 | 0.25 | 0.38 | 0.2 | 0.24 | 0.2 | 0.14 | 0.07 | 0.21 | 0.18 | 0.25 | |
芳烃含量(质量分数)% | / | 0.0197 | 213.7 | ||||||||||
腐蚀试验(100℃,3h)/级 | GB/T5096 | 1b | 1b | 1b | 1b | 1b | |||||||
氧化安定性(150℃)min不小于 | SH/T0193 | 256 | 270 | 272 | 288 | 360 | 375 | 334 | 378 | ||||
蒸发损失(250℃,1h)% | SH/T0059 | 20.51 | 13.9 | 3.0 | 1.17 | 1.92 | 19.2 | 1.02 | |||||
抗乳化度min | 54℃(40-400)不大于 | GB/T7305 | 40-10-0(2min | 40-10-0(2min | 40-40-0(1min40 | 40-40-0(1min30s | 40-40-0(1min30s | 40-40-0(1min) | 40-40-0(4min50s | 40-40-0(1min) | 40-40-0(1min) | ||
低温动力粘度mpa.s | -20℃ | GB/T6538 | -30℃ 9098-20℃2650 | -25℃8977-15℃2510 | 5250(-15℃)3022(-10℃) | -20℃(10118) | -10℃(8100) | ||||||
馏程/℃ | GB/T6536 | 297-336 | 340-397 | 351-457 | 348-423 | 403-483 | 387-478 | 454-547 |